These comfortable gloves have tensile quality of natural rubber, with minimum latex sensitization (reducing the risk of allergy Type I), and offer resistance to a wide range of acids, bases, and alcohol. Gloves of different batches have minimal variation in properties, and provide better consistency as compared to natural rubber.
The new Neoprene formulation ensures increased sensitivity due to the polymer thickness (0.13mm or 5 mil).
Comfort & Fit
Produced on ergonomically-designed hand specific formers to enhance fit and comfort, and to reduce hand fatigue and stress.
Chemical Splash Resistant
Made from 100% polychloroprene, TouchNTuff 73-300 & 73-500 gloves offer chemical splash resistance against a broad range of chemicals.
Reduced Risk of Type I and IV Allergies
Sensitive Neoprene gloves are not manufactured with natural rubber latex or accelerators responsible for end users’ Type I and IV skin allergies, thus reducing the risk of development of such allergies.
No Cuff Roll-Down
Ansell SureFit Technology eliminates “cuff roll down”. By maintaining the glove securely around the arm, Sure Fit Technology provides workers in Life Sciences with more protection during routine lab work and manufacturing by ensuring the efficacy of the gloves as a barrier protection.
Synthetic polyurethane inner coating enables ease of dry and wet hand donning. Design and polymer thickness facilitate ease and comfort of double-gloving, while cream color is a good indicator of breach in double donning applications where other color gloves offer for more safety.
Approved for use with chemotherapy drugs
Sensitive, Chemical Splash Resistant single-use glove, for dry and double donning applications
The sterile version of this TouchNTuff glove made of sensitive Neoprene utilizes thin polychloroprene formulation to offer users superior sensitivity and comfort, ideal for double donning and dry applications. TouchNTuff Sensitive Neoprene gloves offer chemical splash resistance against a wide variety of chemicals. Not made with Natural Rubber Latex or accelerators, it reduces the risk of Type I or IV allergies.
|Glove Design||Anatomic hand specific|
|Sterilization||25 kGy Gamma irradiation|
|Clean Room Compatibility||Gloves are packed in a controlled environment, in a cleanroom-compatible packaging material, which is printed with IPA resistance ink|
|Audit Standards||Manufacturing Facility Registered to ISO 9001, ISO 13485 and ISO 14001|
|Quality Control||Compliant with ASTM D 3577, Type II, Cat. III glove|
|Packaging||One pair per poly wallet, sealed in a poly envelope; 10 pairs per outer polybag; 5 sealed outer polybags per master polybag; 4 sealed master polybags per lined carton; 200 pairs per carton|
|Storage||Cool environment, shielded from ozone and UV light|
|Country of Origin||Sri Lanka|
|Property||Typical values||Testing method|
|SIZE||5.5||6.0||6.5||7.0||7.5||8.0||8.5||9.0||ASTM D3767/EN 420|
|Nominal Length (mm/inches)||305/12||305/12||305/12||305/12||305/12||305/12||305/12||305/12|
|Average Palm Width (mm)||72||77||83||89||95||102||108||114|
|Freedom from Holes (Inspection level I)||1.0 AQL||ASTM D5151/EN 374-2|
|Palm Thickness Single Wall||0.130 mm / 5.0 mils||ASTM D3767/EN 420|
|Particulate Count||≤ 2500 Counts / cm²||IEST-RP-CC005.2-7|
|Endotoxin||10.4 EU/pair of gloves||ASTM D7102|
|Before Aging||After Aging|
|Ultimate Tensile Strength||17||12||ASTM D 412-06a|
|Elongation at Break (%)||650||490||ASTM D 412-06a|
|Modulus @ 500%||7.0 Max||N/A||ASTM D 412-06a|
|Force at break||≥ 9N||≥ 9N||EN 455-2|